ABSTRACT
Objective: To investigate the bone repair and regeneration ability of biomimetic mineralized collagen bone graft material and autologous bone marrow in rabbit posterolateral spinal fusion model. Methods: Twenty-seven 20-week-old male New Zealand white rabbits ［weighing (5.0±0.5) kg］ were used to establish the posterolateral spinal fusion model of L 5 and L 6 segments by stripping the transverse process and exposing cancellous bone with electric burr. The rabbits were randomly divided into 3 groups, 9 in each group. Groups A, B, and C were implanted 1.5 mL autologous iliac bone, 1.5 mL (30 mm×10 mm×5 mm) biomimetic mineralized collagen bone graft material, and 1.5 mL (30 mm×10 mm×5 mm) biomimetic mineralized collagen bone graft material and autologous bone marrow in each bone defect. At 4, 8, and 12 weeks after operation, the apparent hardness of the bone grafting area was observed by manipulation method, in order to evaluate bone graft fusion effects. Three animals were sacrificed in each group at each time point, the vertebral body specimens were excised and the bone defect repair and fusion were observed by X-ray films, and three-dimensional CT examination was performed to evaluate whether new bone was formed in the body. HE staining was performed at each time point to observe the formation of new bone and the repair and fusion of bone defects. Results: The manipulation test showed that bone graft fusion was not found in all groups at 4 weeks after operation; 3 (50.0%), 2 (33.3%), and 4 (66.7%) of groups A, B, and C reached bone graft fusion at 8 weeks after operation; 5 (83.3%), 4 (66.7%), and 5 (83.3%) of groups A, B, and C reached bone graft fusion at 12 weeks after operation; the fusion rate of group C was similar to that of group A, and all higher than that of group B. X-ray film observation showed that the fusion rate of group C at 8 and 12 weeks after operation was higher than that of group B, similar to group A. Three-dimensional CT observation showed that the effect of bone fusion in group C was better than that in group B, which was close to group A. HE staining observation showed that large area of mature lamellar bone coverage appeared in the bone graft area of groups A, B, and C at 12 weeks after operation, the material was completely degraded, and the marginal boundary of the host bone disappeared and tightly combined. Conclusion: Biomimetic mineralized collagen bone graft material mixed with autologous bone marrow has good osteoinduction and osteogenesis guidance. Compared with biomimetic mineralized collagen bone graft material, it has better and faster osteogenesis effect, which is close to autologous bone transplantation.
ABSTRACT
Objective:To study the effects of beta tricalcium phosphate(β-TCP)/collagen scaffold loaded with human bone morphogenetic protein 2 (hBMP2) plasmid on the osteogenesis ability of MC3T3-E1 cells.Methods:hBMP2 DNA plasmid-modified β-TCP/collagen scaffold and the naked plasmid(control) were constructed.MC3T3-E1 cells were respectively in vitro cultured onto the β-TCP/collagen scaffold with hBMP2(Z) and with control plasmid(Z0),on peace dish with the saffold and hBMP2(M) and with the control plasmid(M0).The surface morphology of the samples was observed by SEM.Osteogenesis of the cells was examined by alkaline phosphatase activity(ALP) test,real-time fluorescent quantitative PCR for the detection of Runx2,OCN,ALP and OPN mRNA expression.Data were statistically analyzed.Results:The composite sample surface of plasmid DNA containing hBMP2 modified β-TCP/collagen was porous;group Z and M showed highter ALP activity and higher mRNA expression of Runx2,OCN,ALP and OPN than group Z0 and M0;so did group Z than group M.Conclusion:Porous β-TCP/collagen scaffold loaded with BMP2 DNA is potential for osteoinduction.